“聚碳酸酯二元醇 PCDL(Polycarbonatediol)PCDL 1022”参数说明
形态: | 液体 | 类型: | 多元醇 |
含羟基数: | 二元醇 | 类别: | 不饱和醇 |
型号: | PCDL 1022 | 包装: | 200kg |
“聚碳酸酯二元醇 PCDL(Polycarbonatediol)PCDL 1022”详细介绍
聚碳酸酯二元醇PCDL(Polycarbonatediol) |
|
|
||||||
|
产品参数 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
品名Product Name |
|
|
|
聚碳酸酯二元醇 |
|
|
|
|
|
|
|
|
|
|
|
|
|
型号Product Type |
|
|
|
|
PCDL 1022 |
|
|
|
|
|
|
|
|
|
|
|
|
分子量Molecular Weight |
|
|
|
2000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
外观Appearance |
|
|
|
|
粘稠液体 |
|
|
|
|
|
|
|
|
|
|
|
|
羟基含量Hydroxyl Content % |
|
|
|
1.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
酸值Acidity Value mg KOH/g |
|
|
|
<0.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
色泽Color |
|
|
|
<100 |
|
|
|
|
|
|
|
|
|
|
|
|
|
水分Water Content % |
|
|
|
<0.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
粘度70℃Viscosity cp.s |
|
|
|
1960 |
|
|
|
|
|
|
|
|
|
|
||
|
用各种多元醇制成的聚氨酯的基本特性比较: |
|
|
|
|
|||
|
项目Item |
PCDL |
普通PCDL |
|
PTMEG |
PHA |
|
|
|
|
|
|
|
|
|
|
|
|
耐热性Heat stability |
优 |
优 |
|
差 |
良 |
|
|
|
|
|
|
|
|
|
|
|
|
耐候性Weather ability |
优 |
优 |
|
差 |
良 |
|
|
|
|
|
|
|
|
|
|
|
|
柔软性Softness |
良 |
差 |
|
优 |
良 |
|
|
|
|
|
|
|
|
|
|
|
|
耐水性Hydrolysis resistance |
优 |
优 |
|
良 |
差 |
|
|
|
|
|
|
|
|
|
|
|
|
耐菌性Fungi resistance |
良 |
良 |
|
优 |
差 |
|
|
|
|
|
|
|
|
|
|
|
|
耐油酸性Oleic acid resistance |
良 |
良 |
|
差 |
可 |
|
|
|
|
|
|
|
|
|
|
|
|
耐醇性Ethanol resistance |
良 |
良 |
|
差 |
可 |
|
|
|
|
|
|
|
|
|
|
|
|
用各种多元醇制成的聚氨酯的机械特性比较 |
|
|
|
|
|||
|
|
|
|
|
|
|
|
|
|
项目Item |
PCDL |
PCL |
|
PTMEG |
PHA |
|
|
|
|
|
|
|
|
|
|
|
|
断裂强度(Mpa) |
76-83 |
|
52-64 |
|
66-72 |
53-72 |
|
|
|
|
|
|
|
|
|
|
|
断裂伸长(%) |
580-630 |
|
880-970 |
|
920-1040 |
860-920 |
|
|
|
|
|
|
|
|
|
|
主要特点:
与一般的聚酯,聚醚系的二醇相比,显现出相当优异的机械性能、抗水解性、热稳定性、耐候性和耐溶剂性。
产品应用
人造革、合成革、TPU、TPE、氨纶、胶粘剂、双组份聚氨酯涂料、自修复PU 涂料、水性聚氨酯分散体;弹性手感耐磨涂料等。
提升耐久、耐光、耐化、耐水解、耐磨、耐热、耐热黄变性能,PCDL 将是最佳的选择。
溶解性/稀释
是可以与酯类,酮类,芳香族烃类和醚酯。低固含量溶液长期储存,可能导致浑浊和沉淀。应该使用聚氨酯级溶剂(水分<0.1%,不含其他反应性杂质)